Preparation of Solution Impregnated Continuous Carbon Fibre Reinforced Poly (Phthalazinone Ether Sulfone Ketone) Composites
Article
Gong Xiong Liao1  Xi Gao Jian1  Liang Zheng2 
[1] Department of Polymer Science and materials, Dalian University of Technology, Dalian 116012, China;Drilling & Production Technology Research Institute of Liaohe Oilfield Company, China National Petroleum Corporation, Panjin 124010, China;
关键词: Composites;    Carbon fibre;    PPESK;    Solution impregnate;   
DOI  :  10.1177/096369350901800101
 received in 2008-05-25, accepted in 2009-04-02,  发布年份 2009
来源: Sage Journals
PDF
【 摘 要 】

Continuous carbon fibre reinforced Poly (phthalazinone ether sulfone ketone) (PPESK) composites were prepared using a solution impregnation process and hot-press molding method. The effects of polymer solution viscosities on fibre impregnation, fibre volume fraction and thereby on mechanical properties of composites were studied. The results show that the fibre impregnation and fibre volume fraction decreased with increasing polymer solution viscosities, and the mechanical properties of composites mainly depended on the fibre volume content.

【 授权许可】

Unknown   
© 2009 SAGE Publications Ltd

【 预 览 】
附件列表
Files Size Format View
RO202212209862548ZK.pdf 717KB PDF download
Figure 6. 416KB Image download
Figure 2. 525KB Image download
Fig. 3 65KB Image download
Figure 3. 91KB Image download
Figure 4. 25KB Image download
【 图 表 】

Figure 4.

Figure 3.

Fig. 3

Figure 2.

Figure 6.

【 参考文献 】
  • [1]
  • [2]
  • [3]
  • [4]
  • [5]
  • [6]
  • [7]
  • [8]
  • [9]
  • [10]
  • [11]
  文献评价指标  
  下载次数:7次 浏览次数:0次