Ultrasonic Analysis of Damage in CFRP Resulting from Static Indentation and Low Velocity Impact | |
Article | |
H. Kaczmarek1  | |
[1]Office National d'Etudes et de Recherches Aérospatiales 92320 Châtillon, France | |
关键词: Ultrasounds; Nondestructive testing; Composites (CFRP); Damage; Delamination; Cracking; Low velocity impact; Fractography; Accelerometry; Ultrasonic tomography; | |
DOI : 10.1177/096369359300200304 | |
来源: Sage Journals | |
![]() |
【 摘 要 】
In order to reduce hidden damage caused in CFRP by low velocity transverse impact, testing procedures must be established by understanding the impact phenomena and the roles of various parameters on damage initiation and growth. Hence, composite plates were stressed and an original method, “ultrasonic tomography,” was applied to detect delaminations on the interfaces. The results show the similarity of the damage growth resulting from static indentation and low velocity impact.【 授权许可】
Unknown
© 1993 SAGE Publications Ltd
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202212208641316ZK.pdf | 833KB | ![]() |
【 参考文献 】
- [1]
- [2]
- [3]
- [4]
- [5]