Advanced Composites Letters | |
Preparation and Mechanical Properties of Fe3Al-MWNTs Composites | |
Article | |
Jing Xu1  Laixue Pang1  Jinsheng Zhang1  | |
[1]Department of Civil Engineering, Shandong Jiaotong University, Jinana, 250023, PR China | |
关键词: carbon nanotubes composites; iron aluminides; hot pressing; | |
DOI : 10.1177/096369350801700404 | |
received in 2008-07-24, accepted in 2008-08-26, 发布年份 2008 | |
来源: Sage Journals | |
![]() |
【 摘 要 】
Multiwall carbon nanotubes (MWNT) reinforced iron aluminides (Fe3Al) intermetallic matrix composites have been prepared by a conventional (hot pressing) sintering method. Morphological, structural, compositional and mechanical properties investigations have been performed. Compressive testing shows that the composites still display high yield strength. The first results show that carbon nanotubes have been preserved in composite structure during the sintering process.【 授权许可】
Unknown
© 2008 SAGE Publications Ltd
【 预 览 】
Files | Size | Format | View |
---|---|---|---|
RO202212205487098ZK.pdf | 1071KB | ![]() |
|
Table 2. | 742KB | Table | ![]() |
Figure 5. | 199KB | Image | ![]() |
Figure 8. | 554KB | Image | ![]() |
Figure 6. | 195KB | Image | ![]() |
Figure 7. | 223KB | Image | ![]() |
Table 1 | 73KB | Table | ![]() |
Figure 8. | 210KB | Image | ![]() |
Table 3 | 63KB | Table | ![]() |
【 图 表 】
Figure 8.
Figure 7.
Figure 6.
Figure 8.
Figure 5.
【 参考文献 】
- [1]
- [2]
- [3]
- [4]
- [5]
- [6]
- [7]
- [8]
- [9]
- [10]
- [11]
- [12]
- [13]
- [14]
- [15]
- [16]
- [17]
- [18]
- [19]
- [20]