Effect of Water Absorption on the Mechanical Properties of Pultruded Kenaf Fibre Reinforced Polyester Composites
Article
Z.A. Mohd Ishak1  Norlin Nosbi1  Hazizan Md. Akil1  Azhar A. Bakar1 
[1] School of Material and Mineral Resources Engineering, Universiti Sains Malaysia, 14300 Seberang Perai Selatan, Pulau;
关键词: kenaf fibre;    fibre reinforced polymers (FRPs);    water absorption;    pultrusion;   
DOI  :  10.1177/096369351102000103
 received in 2010-07-22, accepted in 2010-07-30,  发布年份 2011
来源: Sage Journals
PDF
【 摘 要 】

Kenaf fibre reinforced polyester composites (KFRPC) were prepared using pultrusion method with 30:70 matrix to fibre ratio. The effect of water absorption 260 days in distilled water at room temperature on the mechanical properties was evaluated. Test results indicated KFRPC strengths had decreased with increase in percentage of water uptake. The moisture absorption leads the degradation and creating poor stress transfer efficiencies resulting in a reduction of mechanical properties.

【 授权许可】

Unknown   
© 2011 SAGE Publications Ltd

【 预 览 】
附件列表
Files Size Format View
RO202212203324968ZK.pdf 1019KB PDF download
Table 2. 584KB Table download
Figure 4. 421KB Image download
Figure 3. 42KB Image download
Figure 4. 89KB Image download
Figure 5. 241KB Image download
Table 4. 955KB Table download
Table 4. 119KB Table download
Figure 9. 125KB Image download
Figure 4. 499KB Image download
【 图 表 】

Figure 4.

Figure 9.

Figure 5.

Figure 4.

Figure 3.

Figure 4.

【 参考文献 】
  • [1]
  • [2]
  • [3]
  • [4]
  • [5]
  • [6]
  • [7]
  • [8]
  • [9]
  • [10]
  • [11]
  • [12]
  • [13]
  • [14]
  • [15]
  • [16]
  • [17]
  • [18]
  • [19]
  • [20]
  文献评价指标  
  下载次数:1次 浏览次数:3次