Influence of alternating magnetic field on microstructure and mechanical properties of laser-MIG hybrid welded HG785D steel joint

Journal of Materials Research and Technology

Xiaoguo Song¹  Caiwang Tan²  Bo Chen²  Biao Yang³  Laijun Wu³  Hongyun Zhao³  Fuyun Liu³ 

[1] Corresponding author.;Shandong Institute of Shipbuilding Technology, Weihai 264209, China;State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China;

关键词: Laser-MIG hybrid welding;    Alternating magnetic field;    Microstructure;    Mechanical properties;    Hybrid welding plasma;   

DOI  :  

来源: DOAJ

【 摘 要 】

The work aimed to investigate the effects of alternating magnetic field on the microstructure, mechanical properties and plasma characteristics during laser-MIG hybrid welding of HG785D steel. The weld appearance was improved and the weld depth was significantly enhanced by an alternating magnetic field. The same microstructure type of lath martensite (LM) was obtained in the arc zone and laser zone of all hybrid welded joints. However, grains in the arc zone were significantly refined and the ratio of high-misorientation angles was increased under alternating magnetic field. The average grain size in the arc zone reduced from 4.60 to 3.67 μm with a magnetic flux density of 30 mT. The average microhardness of the arc part and the laser part increased from 356 and 378 to 388 and 393 HV, respectively. The grain refinement and increased ratio of high-misorientation angles led to an improvement in low-temperature impact toughness. The low-temperature impact toughness was 184 J with a magnetic flux density of 30 mT, which was 95.7% higher than that without the alternating magnetic field. Additionally, the shielding effect of the hybrid plasma was suppressed with the magnetic flux density of 10–30 mT, leading to an increase in the penetration ability of hybrid heat sources and weld depth. However, the penetration ability of the hybrid heat source was no longer enhanced with a further increase in magnetic flux density.