Using Neutron Diffraction to Investigate Texture Evolution During Consolidation of Deuterated Triaminotrinitrobenzene (d-TATB) Explosive Powder

Crystals

Amanda L. Higginbotham Duque¹  John D. Yeager¹  Bjørn Clausen²  Donald W. Brown²  Sven C. Vogel²  Darby J. Luscher³ 

[1] Explosive Science and Shock Physics Division, Los Alamos National Laboratory, Los Alamos, NM 87545, USA;Material Science and Technology Division, Los Alamos National Laboratory, Los Alamos, NM 87545, USA;Theoretical Division, Los Alamos National Laboratory, Los Alamos, NM 87545, USA;

关键词: neutron diffraction;    texture;    triaminotrinitrobenzene (TATB);    powder compaction;    triclinic;   

DOI  :  10.3390/cryst7050138

来源: DOAJ

【 摘 要 】

Triaminotrinitrobenzene (TATB) is a highly anisotropic molecular crystal used in several plastic-bonded explosive (PBX) formulations. A complete understanding of the orientation distribution of TATB particles throughout a PBX charge is required to understand spatially variable, anisotropic macroscale properties of the charge. Although texture of these materials can be measured after they have been subjected to mechanical or thermal loads, measuring texture evolution in situ is important in order to identify mechanisms of crystal deformation and reorientation used to better inform thermomechanical models. Neutron diffraction measurements were used to estimate crystallographic reorientation while deuterated TATB (d-TATB) powder was consolidated into a cylindrical pellet via a uniaxial die-pressing operation at room temperature. Both the final texture of the pressed pellet and the in situ evolution of texture during pressing were measured, showing that the d-TATB grains reorient such that (001) poles become preferentially aligned with the pressing direction. A compaction model is used to predict the evolution of texture in the pellet during the pressing process, finding that the original model overpredicted the texture strength compared to these measurements. The theory was extended to account for initial particle shape and pore space, bringing the results into good agreement with the data.