Effect of Niobium on Inclusions in Fe-Mn-C-Al Twinning-Induced Plasticity Steel

Metals

Changling Zhuang¹  Fangjie Lan¹  Changrong Li¹  Wenhui Du¹ 

[1] College of Materials and Metallurgy, Guizhou University, Guiyang 550025, China;

关键词: TWIP steel;    thermodynamics;    inclusion;    precipitation behavior;   

DOI  :  10.3390/met11010083

来源: DOAJ

【 摘 要 】

The effect of Nb addition on the composition, morphology, quantity, and size of inclusions in Fe-Mn-C-Al steel was studied by SEM, EDS, and thermodynamic analysis. The research shows that the number of inclusions in Fe-Mn-C-Al high manganese steel decreases obviously after adding 0.04% element Nb, and some inclusions in the steel evolve into complex niobium inclusions. When the niobium content increases to 0.08%, the influence of niobium on inclusions in steel becomes more obvious. The precipitation temperature of inclusions in Fe-Mn-C-Al steel was analyzed by thermodynamics. The results show that the nucleation core of the composite inclusions is AlN, and then NbC and MnS precipitate locally on its surface. With the increase of Nb, the amount and volume fraction of NbC inclusions precipitated in steel increase.

【 授权许可】

Unknown