Influence of High Temperature Curing and Surface Humidity on the Tensile Strength of UHPC

Materials

Matthias Kalthoff¹  Thomas Matschei¹  Michael Raupach¹ 

[1] Institute of Building Materials Research (IBAC), RWTH Aachen University, Schinkelstraße 3, 52062 Aachen, Germany;

关键词: direct tensile strength;    ultra-high-performance concrete (UHPC);    autoclaving;    heat treatment;   

DOI  :  10.3390/ma14154260

来源: DOAJ

【 摘 要 】

The objective of this study is an investigation of the different parameters that influence the tensile strength of ultra-high performance concrete (UHPC). Apart from the shrinkage and stiffness, the tensile strength is an important parameter for the design of crack-free concrete elements, e.g., in machine tool construction. One focus of our work is the influence of concrete curing and the great impact of the mechanical and physical characteristics of hydrated UHPC. For this reason, different curing regimes were investigated. The results show that even after heat treatment or autoclaving, the centric tensile strength of UHPC specimens is strongly influenced by the surrounding ambient humidity. Test specimens that were stored under water after a heat treatment or autoclaving and were still wet during the test had the highest tensile strengths. Storage at 20 °C and 65% relative humidity (rH), however, results in a 25% reduction in tensile strength. Alternating storage between water storage at 20 °C water and storage at 65% rH can also reduce the tensile strength dramatically by up to 70%. In particular, samples that were stored at 65% rH right before testing had very low tensile strengths. Surprisingly, the initially low tensile strength of previously dry stored UHPC can be restored by subsequent water storage. In the absence of any microstructural defects, e.g., microcracks, a possible explanation for this phenomenon can be the stress differences due to a humidity gradient between the core and surfaces and shrinkage combined with a continued reaction of the unhydrated binders of the UHPC.

【 授权许可】

Unknown