Effect of Alloying Elements Gradient on Solid-State Diffusion Bonding between Aerospace Aluminum Alloys

Materials

Hongliang Hou¹  Yanjin Xu¹  Yujie Han¹  Wenlong Zhou²  Xuesong Fu²  Fan Wu² 

[1] AVIC Aeronautical Manufacturing Technology Research Institute, Beijing 100024, China;School of Material Science and Engineering, Dalian University of Technology, Dalian 116085, China;

关键词: diffusion bonding;    interface microstructure;    shear strength;    alloying element diffusion;   

DOI  :  10.3390/ma11081446

来源: DOAJ

【 摘 要 】

Three different bonding couples assembled by two commonly used aerospace aluminum alloys were bonded within the temperature range of 460–520 °C under 6 MPa for 60 min in vacuum atmosphere. The interface microstructure and alloying elements distribution of the bonded joints were determined by scanning electron microscope (SEM) and Energy Dispersive Spectroscope (EDS); the bond strength was evaluated by tensile-shear strength test. The results show the bond quality improved effectively as the bonding temperature increased. Compared with the 1420-1420 and 7B04-7B04 bonding couples, the 1420-7B04 couples obtained better interface integrity and higher bond strength, the highest shear strength for 1420-7B04 couple can be as high as 188 MPa when bonded at 520 °C. Special attention was focused on the 1420-7B04 couple, the diffusion coefficient of Mg at the original interface under different temperatures were investigated, the results show the diffusion coefficient increased obviously as the bonding temperature increased. A diffusion affected zone (DAZ) without continuous intermetallic phases formed due to the diffusion of alloying elements across the bonding interface. The combined action of temperature and alloying elements gradient resulted in the increase of alloying elements diffusion fluxes, which in turn promote the bonding quality through the accelerated shrinkage of interfacial voids.

【 授权许可】

Unknown