Mechanical Properties of Glass-Based Geopolymers Affected by Activator and Curing Conditions under Optimal Aging Conditions
Tai-An Chen1 
[1] Department of Harbor and River Engineering, National Taiwan Ocean University, No. 2, Pei-Ning Rd., Zhongzheng Dist., Keelung City 202301, Taiwan;
关键词: waste glass;    inorganic binder;    curing temperature;    curing duration;   
DOI  :  10.3390/cryst11050502
来源: DOAJ
【 摘 要 】

Inorganic polymeric materials react slowly at room temperature and therefore, usually require high-temperature curing. This study determined the correlation between temperature and duration in high-temperature curing. The results revealed optimal values for each alkali equivalent of an activator (weight ratio of Na2O/glass powder), curing temperature, and curing duration. Increasing the curing duration and curing temperature had positive effects when the alkali equivalent was lower than the optimal percentage. However, over-curing resulted in the visible cracking of the specimens. Furthermore, despite being initially high, the compressive strength of specimens gradually diminished after standing in air. To ensure the durability of glass-based geopolymers, the curing temperature and duration should not exceed 70 °C, and 1 day, respectively.

【 授权许可】

Unknown   

  文献评价指标  
  下载次数:0次 浏览次数:2次