Electromagnetic characterization of Ni0.5Zn0.3Co0.2Fe2O4 bulk ceramics in the 1MHz-12GHz frequency range

Processing and Application of Ceramics

Machado João Paulo Barros¹  de Morais Santos Júlia Maria²  de Brito Vera Lúcia Othéro²  Carvalho Francisco Eduardo de³  Bormio-Nunes Cristina⁴ 

[1] Instituto Nacional de Pesquisas Espaciais, Laboratório Associado de Sensores e Materiais, Jardim da Granja, São José dos Campos, Brazil;Instituto de Estudos Avançados, Divisão de Fotônica, São José dos Campos, Brazil;Instituto de Estudos Avançados, Divisão de Física Aplicada, São José dos Campos, Brazil;Universidade de São Paulo, Faculdade de Engenharia Química de Lorena, Lorena, Brazil;

关键词: ferrites;    solid state synthesis;    magnetic properties;    dielectric properties;    soft magnets;   

DOI  :  10.2298/PAC2102136B

来源: DOAJ

【 摘 要 】

In this paper, NiZnCo ferrite was produced by solid state synthesis, calcination at 1000°C and sintering at 1250°C in air atmosphere. The microstructure and phases of the sintered sample were analysed by scanning electron microscopy and X-ray diffraction, respectively. The magnetic properties of the ferrite were evaluated by magnetization and magnetostriction measurements. The complex magnetic permeability and complex permittivity were also measured between 1MHz-12GHz and the reflection loss (RL) was calculated in the 100MHz-12GHz frequency range. The results show that the ferrite sample presents magnetostrictive behaviour and a saturation magnetization of 71 Am2/kg. Complex permittivity measurements indicate that the material has dielectric behaviour in the whole frequency range studied, with "′ varying between 7-40, and magnetic behaviour in frequencies between 1MHz-5GHz. The minimum RL was found at frequencies between 2.4-3.3GHz and the calculated RL value for a thickness of 3mm was lower than −10 dB in frequencies between 2.3-7.3GHz. These results indicate potential application as microwave absorber in the S band.