Evaluation of Fracture Strength of Ceramics Containing Small Surface Defects Introduced by Focused Ion Beam

Materials

Koji Takahashi¹  Nanako Sato² 

[1] Faculty of Engineering, Yokohama National University, 79-5 Tokiwadai, Hodogaya, Yokohama 240-8501, Japan;Graduate School of Engineering, Yokohama National University, 79-5 Tokiwadai, Hodogaya, Yokohama 240-8501, Japan;

关键词: Al2O3/SiC;    focused ion beam;    surface defect;    fracture strength;    process zone size failure criterion;    area parameter model;   

DOI  :  10.3390/ma11030457

来源: DOAJ