Investigations of Forming Mixture Parameters of Autoclaved Aerated Concrete with Nanoadditives

Medžiagotyra

Lina LEKŪNAITĖ¹  Donatas MIKULSKIS¹  Modestas KLIGYS¹  Antanas LAUKAITIS¹ 

[1] Vilnius Gediminas Technical University;

关键词: autoclaved aerated concrete;    amorphous SiO2;    crushed carbon fiber;    nanoadditive;    spreadability;    expansion;    temperature;    plasticity strength;    UIV;   

DOI  :  10.5755/j01.ms.18.3.2441

来源: DOAJ

【 摘 要 】

Impact of some nanoadditives, such as amorphous SiO₂ (AS) of pozzolanic properties and carbon fibers (CF) reduced to nanosize particles on autoclaved aerated concrete (AAC) forming mixtures, the following parameters were investigated: changes in consistence of binding material during hydration, spreadability, expansion and temperature of mixture, plasticity strength. The investigations were carried out with AAC forming mixture where 10 % lime was replaced by equivalent content of Portland cement. Upon completion of investigations, it was established that the optimal replacement of sand by AS was 1.0 % resulting in increase of temperature of AAC forming mixture by up to 2.1 %, expansion by up to 11.0 %, ultrasonic impulse velocity (UIV) by up to 3.0 % and plasticity strength by up to 271.4 %. Meanwhile the optimal replacement of sand by CF was 0.1 % resulting in decrease in temperature of AAC forming mixture by up to 1.5 %, expansion by up to 16.0 % and increase in  UIV by up to 2.0% and plasticity strength by up to 152.9 %.

DOI: http://dx.doi.org/10.5755/j01.ms.18.3.2441