Properties of Jet-Plated Ni Coating on Ti Alloy (Ti6Al4V) with Laser Cleaning Pretreatment

Metals

MuhammadNaveed Ahsan¹  Changjiang Wang²  Xiao Wang³  Zongjun Tian³  Zhanwen Wang³  Lida Shen³  Mingyang Xu³  Mingbo Qiu³ 

[1] Center of Excellence in Science and Applied Technologies, Sector H-11, Islamabad 44000, Pakistan;Department of Engineering and Design, University of Sussex, Sussex House, Brighton BN1 9RH, UK;National Key Laboratory of Science and Technology on Helicopter Transmission, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China;

关键词: laser cleaning;    titanium alloy;    jet electrodeposition;    friction properties;   

DOI  :  10.3390/met9020248

来源: DOAJ

【 摘 要 】

The surface mechanical properties of the Selective Laser Melting (SLM) formed Ti6Al4V samples were improved by adopting a novel laser cleaning pretreatment process combined with a jet electrodeposition process. This paper aimed to investigate the effects of different laser powers on the morphologies and adhesions of the nickel coatings. The advantages of the laser cleaning process are no grinding, no contact, high efficiency and environmental protection. The morphologies, adhesion, wear resistance, and hardness of the coatings were characterized. The results indicate that when the laser energy density reached 20% (4 J/cm²), the contaminations on the substrate and the oxide layer were removed and the crystalline grain of the coating was 15.3 nm. The shallow pits generated by laser burning increased the adhesion of the coatings. In addition, when the laser energy density increased to 6 J/cm², a yellow oxide layer was produced on the surface of the cleaned titanium alloy. Moreover, the wear resistance of the titanium alloy after the nickel plating was improved. The wear volume was only 0.046 mm³, and the hardness increased to 1967.6 N/mm².

【 授权许可】

Unknown