Preparation of a Near-Infrared Ray Absorption Film from N-Phenylthiocarbamoyl Chitosan Derivative

International Journal of Molecular Sciences

Masaya Shibano¹  Hiroshi Kamitakahara¹  Shouko Nishida¹  Toshiyuki Takano¹ 

[1] Division of Forest and Biomaterials Science, Graduate School of Agriculture, Kyoto University, Kyoto 606-8502, Japan;

关键词: chitosan;    copper;    decanoylation;    near-infrared absorption;    phenythiocarbamoyl;   

DOI  :  10.3390/ijms161226153

来源: DOAJ

【 摘 要 】

We recently observed that the decanoylation of N-phenylthiocarbamoyl chitosan (2)with a mixture of decanoic anhydride and pyridine at 60 °C for 24 h affordedN,N-(decanoyl)phenythiocarbamoyl-/2-isothiocynato chitosan decanoate (3b) rather than the expected product N,N-(decanoyl)phenylthiocarbamoyl chitosan decanoate (3a). This result suggested that some of the N,N-(decanoyl)phenylthiocarmbamoyl groups had been converted to isothiocyanate groups during the decanoylation process. The subsequent reaction of compound 3b with aniline gave N,N-(decanoyl)phenylthiocarbamoyl/N-phenylthiocarbamoyl chitosan decanoate (4) in high yield. A solution of compound 4 in CHCl3 was then added to a solution of copper decanoate (5) in the same solvent, and the resulting mixture was cast onto a glass plate to give a cast film. The film was annealed at 200 °C in an oven to give a greenish film, which showed goodnear-infrared absorption characteristic in the range of 800–2200 nm.

【 授权许可】

Unknown