Numerical simulation of central shrinkage crack formation in a 234-t steel ingot

China Foundry

Hou-fa Shen¹  Yue-qiao Wang¹  Jing-an Yang² 

[1] Casting and Forging Workshop, China National Erzhong Group Co. Ltd., Deyang 618000, China;School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China;

关键词: shrinkage crack;    finite-element;    crack potential;    thermo-mechanical simulation;    steel ingot;   

DOI  :  10.1007/s41230-017-7160-5

来源: DOAJ

【 摘 要 】

Central shrinkage crack is a common defect encountered in steel ingot casting. It is necessary to limit the degree of crack in case of further propagation in forging. A 234-t steel ingot was dissected to check the internal quality, and a central shrinkage crack band of 1,400 mm in height and 120 mm in width, was found at a distance of 450 mm under the riser bottom line. Then, thermo-mechanical simulation using an elasto-viscoplastic finite-element model was conducted to analyze the stress-strain evolution during ingot solidification. A new criterion considering mush mechanical property in the brittle temperature range as well as shrinkage porosity was used to identify the shrinkage crack potential, where the degree of shrinkage porosity is regarded as a probability factor using a modified sigmoid function. Different casting processes, such as pouring speed, mould preheating and riser insulation, were optimized with the simulation model. The results show that fast pouring, proper mould preheating and good riser insulation can alleviate shrinkage crack potential in the ingot center.

【 授权许可】

Unknown