Microstructure Evolution and Mechanical Properties of the 2195 Al-Li Alloy via Different Annealing and Ramp Heating-Up Treatments

Metals

Yun-Long Ma¹  Jin-Feng Li²  Dan-Yang Liu²  Tian-Le Liu² 

[1] Beijing Institute of Astronautical Systems Engineering, Beijing 100076, China;School of Materials Science and Engineering, Central South University, Changsha 410083, China;

关键词: Al-Li alloy;    microstructure evolution;    grain structure;    preannealing;    tensile property;   

DOI  :  10.3390/met10070910

来源: DOAJ

【 摘 要 】

In this paper, the microstructure evolution of the 2195 Al-Li alloy under different isothermal annealing schedules and ramp heating-up heat treatments prior to solution heat treatment and the tensile properties of the aging alloy were investigated. The grain structure characteristics of the aging alloy could be influenced by the change of different heat treatment schedules prior to the solution heat treatment. Meanwhile, the mechanical properties of the aging alloy including strength, heterogeneity, and anisotropy were closely related to the grain structure characteristics. There were evident differences in the mechanical properties of aging samples, attributed to the mutual effect of grain structure evolution and texture change. Annealing at a lower temperature (300–350 °C) resulted in the growth of the grain size and the aspect ratio as well as the decrease of the deformation texture components, related to the decline of the strength and the heterogeneity. While grains refined and the deformation texture components increased as the annealing temperature rose (350–400 °C), the strength along the transverse direction decreased, and the heterogeneity increased. Fibrous and overall texture components significantly strengthened in the grain structure of aging samples treated with the low heating-up rate, resulting in a higher strength in the longitudinal direction.

【 授权许可】

Unknown