Comparison of low and high frequency fatigue tests

Production Engineering Archives

Vaško Alan¹  Belan Juraj¹  Kuchariková Lenka¹ 

[1] University of Žilina, Faculty of Mechanical Engineering, Department of Materials Engineering, Univerzitná 8215/1, 010 26Žilina, Slovakia;

关键词: fatigue test;    low frequency cyclic loading;    high frequency cyclic loading;    nodular cast iron;   

DOI  :  10.30657/pea.2017.17.03

来源: DOAJ

【 摘 要 】

The paper presents the results of low and high frequency fatigue tests carried out on nodular cast iron. The specimens of synthetic nodular cast irons from three different melts were studied in the high cycle fatigue region (from 105 to 108 cycles) using fatigue experimental equipments for low and high frequency cyclic loading. Low frequency fatigue tests were carried out at frequency f ≈ 120 Hz using the fatigue experimental machine Zwick/Roell Amsler 150HFP 5100; high frequency fatigue tests were carried out at frequency f ≈ 20 kHz using the ultrasonic fatigue testing device KAUP-ZU. Both fatigue tests were realised at sinusoidal cyclic push-pull loading (stress ratio R = −1) at ambient temperature (T = 20 ± 5 °C).

【 授权许可】

Unknown