Enhancement of Spontaneous Polarization and Acid Vapor-Induced Polymerization in the Thin-Film States of Phenylterthiophene Derivative Bearing a Cyclotetrasiloxane Ring

Crystals

Jumpei Nakagawa¹  Masahiro Funahashi¹  Atsushi Seki¹ 

[1] Program in Advanced Materials Science, Faculty of Engineering and Design, Kagawa University, 2217-20 Hayashi-cho, Takamatsu, Kagawa 761-0396, Japan;

关键词: liquid-crystalline semiconductor;    ferroelectric liquid crystal;    spontaneous polarization;   

DOI  :  10.3390/cryst10110983

来源: DOAJ

【 摘 要 】

We have achieved the measurement of spontaneous polarization of spin-coated thin films of a ferroelectric liquid crystal based on a phenylterthiophene skeleton. Uniaxially aligned spin-coated films with a thickness of 100 nm were prepared by the friction transfer method. The spontaneous polarization of the spin-coated films was measured by the Sawyer–Tower method and polarization inversion current technique under the application of triangular-wave bias. These measurements revealed the spontaneous polarization of 50 nC cm⁻² in the thin-film state which is 1.5 times larger than the value of 35 nC cm⁻² in the bulk state. This result should be attributed to the strong anchoring of the liquid-crystalline molecules on the substrate surface and the inhibition of polarization relaxation caused by the formation of the helical structure. Moreover, insolubilization of the thin films was carried out by an in situ ring-opening polymerization induced by acid vapors. The molecular alignment in the thin films of the ferroelectric liquid crystal was retained during the polymerization process.

【 授权许可】

Unknown