Embedded three spinel ferrite nanoparticles in PES-based nano filtration membranes with enhanced separation properties

Main Group Metal Chemistry

BandehAli Samaneh¹  Moghadassi Abdolreza¹  Ghanbari Davood² 

[1] Department of Chemical Engineering, Faculty of Engineering, Arak University, Arak38156-8-8349, Iran;Department of Science, Arak University of Technology, Arak, Iran;

关键词: ferrite nanoparticles;    nanofiltration membrane;    separation performance;    heavy metal removal;   

DOI  :  10.1515/mgmc-2022-0001

来源: DOAJ

【 摘 要 】

In this study, three types of ferrites nanoparticles including CoFe2O4, NiFe2O4, and ZnFe2O4 were synthesized by microwave-assisted hydrothermal method. The X-ray diffraction analysis (XRD), Fourier transform infrared spectroscopy (FTIR), and field emission scanning electron microscopy (FESEM) were employed to analyze synthesized nanoparticles and fabricated membranes. The morphology of membrane surface was investigated by surface images. The ability of ferrite nanoparticles was evaluated to the separation of sodium salt and heavy metals such as Cr2+, Pb2+, and Cu2+ from aqueous solutions. The modified membrane showed the enhancement of membrane surface hydrophilicity, porosity, and mean pore size. The results revealed a significant increase in pure water flux: 152.27, 178, and 172.68 L·m−2·h−1 for PES/0.001 wt% of CoFe2O4, PES/0.001 wt% NiFe2O4, and PES/0.001 wt% ZnFe2O4 NPs, respectively. Moreover, Na2SO4 rejection was reached 78% at 0.1 wt% of CoFe2O4 NPs. The highest Cr (II) rejection obtained 72% for PES/0.001 wt% of NiFe2O4 NPs while it was 46% for the neat PES membrane. The Pb(II) rejection reached above 75% at 0.1 wt% of CoFe2O4 NPs. The Cu(II) rejection was obtained 75% at 0.1 wt% of CoFe2O4 NPs. The ferrite NPs revealed the high potential of heavy metal removal in the filtration membranes.

【 授权许可】

Unknown