Experimental and numerical investigations on damage accumulation and energy dissipation of patch-repaired CFRP laminates under repeated impacts

Materials & Design

Ying Tie¹  Cheng Li²  Zhenhui Sun³ 

[1] School of Mechanical and Power Engineering, Zhengzhou University, Science Road 100, Zhengzhou 450001, China;Corresponding authors.;School of Mechanical and Power Engineering, Zhengzhou University, Science Road 100, Zhengzhou 450001, China;

关键词: CFRP laminates;    Patch repair;    Repeated impacts;    Damage accumulation;    Energy dissipation;   

DOI  :  

来源: DOAJ

【 摘 要 】

In this study, the impact response, damage accumulation, interlaminar and intralaminar energy dissipation distributions of patch-repaired carbon fiber reinforced polymer (CFRP) laminates under repeated impacts were studied by combining experimental and numerical methods. A three-dimensional finite element model (FEM) based on continuum damage mechanics (CDM) and cohesive zone model (CZM) was performed using ABAQUS/Explicit to simulate the impact experiments (at impact energy of 10 J ~ 20 J). The influence of impact energy (5 J ~ 15 J) on damage accumulation, interlaminar and intralaminar energy dissipation was explored by numerical calculations. It was found that the sudden drop of the force-time curve was an important signal of serious internal damage of the patch; at impact energy of 5 J ~ 12.5 J, the impact parameters such as impact time, peak force and maximum deflection increased with the increase of impact times; at impact energy of 5 J ~ 12.5 J, the delamination damage after the first impact and the corresponding interlaminar energy dissipation increased slightly with the increase of impact times; the delamination damage can be used as an important factor to reflect the damage accumulation degree of patch-repaired laminates under repeated impacts.

【 授权许可】

Unknown