Modification of Ag8SnS6 Photoanodes with Incorporation of Zn Ions for Photo-Driven Hydrogen Production

Catalysts

Lin-Ya Yeh¹  Kong-Wei Cheng¹ 

[1] Department of Chemical and Materials Engineering, Chang Gung University, Taoyuan 33302, Taiwan;

关键词: hydrogen production;    metal sulfide;    photoelectrochemical performance;    hall measurement;    optical properties;   

DOI  :  10.3390/catal11030363

来源: DOAJ

【 摘 要 】

In this study, Zn ions were incorporated into Ag₈SnS₆ thin films on glass and indium–tin–oxide-coated glass substrates using chemical bath deposition. Detailed procedures for the growth of Ag–Zn–Sn–S semiconductor films and their optical, physical and photoelectrochemical performances were investigated. X-ray diffraction patterns of samples revealed that kesterite Ag₂ZnSnS₄ phase with a certain amount of Ag₈SnS₆ phase can be obtained using ethylenediaminetetraacetic acid disodium salt and trisodium citrate as the chelating agent couples. Images of field-emission scanning electron microscope showed that plate-like microstructures with some spherical aggregates were observed for the sample at low Zn content. It changed to irregular spherical grains with the [Zn]/[Sn] ratios being higher than 0.95 in samples. The energy band gaps of the samples were in the range of 1.57–2.61 eV, depending on the [Zn]/[Sn] molar ratio in sample. From the Hall measurements, the carrier concentrations and mobilities of samples were in the ranges of 6.57 × 10¹²–1.76×10¹⁴ cm⁻³ and 7.14–39.22 cm²/V·s, respectively. All samples were n-type semiconductors. The maximum photoelectrochemical performance of sample was 1.38 mA/cm² in aqueous 0.25 M K₂SO₃ and 0.35 M Na₂S solutions.

【 授权许可】

Unknown