Reconditioning of Diamond Coated Tools and Its Impact on Cutting Performance for CFRP Laminates

Applied Sciences

Akira Okada¹  Alexander Soldatov¹  Alexey Remnev² 

[1] Graduate School of Natural Science and Technology, Okayama University, 3-1-1, Tsushimanaka, Kitaku, Okayama 700-8530, Japan;ITAC Ltd., Group of ShinMaywa Industries, 1-1, Shinmeiwa, Takarazuka 665-0052, Japan;

关键词: cutting tool reconditioning;    decoating;    CVD diamond film;    CFRP;    flank wear;    delamination;   

DOI  :  10.3390/app12031288

来源: DOAJ

【 摘 要 】

In recent years, CVD diamond-coated tungsten carbide (WC-Co) tools have been widely utilized due to their benefits in the machining of non-ferrous alloys and polymer composite materials, especially carbon-fiber-reinforced plastics (CFRPs). The reconditioning of such coated tools is economically attractive due to their high cost and short tool life. The decoating of the remaining diamond film from the used tools and the subsequent surface preparation by wet chemical pretreatment are essential steps for new CVD diamond film formation. Previously, it was shown that reactive ion beam etching (RIBE) could effectively remove CVD diamond films. However, some degree of WC-Co tool substrate damage is expected due to the high ion energy in RIBE and the chemical activity in wet etching. This study addresses the effects of RIBE decoating and surface pretreatment steps on WC-Co tools with a complex shape in terms of the ion-induced surface damage, geometry alteration, and adhesion of a subsequently re-applied CVD diamond film. Moreover, the cutting performance of the tools subjected to the RIBE decoating and repeated film deposition was studied via CFRP cutting tests. It has been shown that the RIBE decoated and recoated tools had a high level of cutting performance comparable to the new tools.

【 授权许可】

Unknown