Structure and Mechanical Properties of the 18Ni300 Maraging Steel Produced by Spark Plasma Sintering

Metals

Angelina Strakosova¹  Filip Průša¹  Alena Michalcová¹  Dalibor Vojtěch¹ 

[1] Department of Metals and Corrosion Engineering, University of Chemistry and Technology, Prague, Technická 5, 166 28 Prague 6, Czech Republic;

关键词: maraging steel 18Ni300;    spark plasma sintering;    heat treatment;    mechanical properties;    microstructure;   

DOI  :  10.3390/met11050748

来源: DOAJ

【 摘 要 】

In this work, a new approach for compaction of the gas-atomized 18Ni300 maraging steel at two different temperatures of 1050 °C and 1150 °C using a progressive SPS technology is studied. Moreover, the influence of two heat treatments combining solution annealing and aging (SAT) and simply aging treatment (AT) on the microstructure and mechanical properties is investigated. It is found that samples compacted at 1050 °C had higher porosity compared to the almost non-porous material produced at 1150 °C. In addition, the difference of 100 °C for the compaction temperature successfully reduces the porosity from 0.86% down to 0.08%. Additionally, we discovered that the higher the compaction temperature, the higher the amount of retained γ-Fe which positively affects the ductility of the samples. The subsequential heat treatment results in precipitation strengthening via the Ni₃Mo precipitates. Microhardness of the SPS1050 and SPS1150 samples increase from 303 ± 13 HV0.1 and 360 ± 5 HV0.1 to 563 ± 31 HV0.1 and 606 ± 17 HV0.1, respectively. The sample compacted at 1150 °C shows the highest ultimate tensile strengths reaching up to 1940 ± 6 MPa, while also showing 4% ductility.

【 授权许可】

Unknown