A Study on the Improvement of the Fatigue Life of Bearings by Ultrasonic Nanocrystal Surface Modification Technology

Metals

Jeong-Hyeon Park¹  Young-Sik Pyun¹  Auezhan Amanov¹  Shirmendagva Darisuren² 

[1] Department of Mechanical Engineering, Sun Moon University, Chungcheongnam-do 31460, Korea;Graduate School, Department of Mechanical Engineering, Sun Moon University, Chungcheongnam-do 31460, Korea;

关键词: needle roller bearing;    surface roughness;    surface hardness;    rolling contact fatigue;    ultrasonic nanocrystal surface modification;   

DOI  :  10.3390/met9101114

来源: DOAJ

【 摘 要 】

In this study, the effects of ultrasonic nanocrystal surface modification (UNSM) technology on the fatigue life of needle roller bearings were investigated. The fatigue life of the untreated and UNSM-treated needle roller bearings was evaluated using a roller fatigue tester at various contact stress levels, under oil lubrication conditions. It was found that the fatigue life of the UNSM-treated needle roller bearing was extended by approximately 34.3% in comparison with the untreated one. The results of the surface roughness and surface hardness of the needle roller bearings before and after UNSM technology were compared and discussed in order to understand the role of UNSM technology in improving fatigue life. It was found that the application of UNSM technology to the needle roller bearings can improve their fatigue life by reducing the friction coefficient and increasing the wear resistance, which may be attributed to the reduction in surface roughness from 0.50 µm to 0.15 µm and also the increase in surface hardness from 58 HRC to 62 HRC.