Comparison and ranking of superelasticity of different austenite active nickel-titanium orthodontic archwires using mechanical tensile testing and correlating with its electrical resistivity

Journal of Pharmacy and Bioallied Sciences

关键词: Electrical resistivity tests;    mechanical tensile testing;    nickel-titanium orthodontic wires;    ranking;   

DOI  :  10.4103/0975-7406.191972

来源: DOAJ

【 摘 要 】

Introduction: The application of light and continuous forces for optimum physiological response and the least damage to the tooth supporting structures should be the primary aim of an orthodontist. Nickel-titanium (NiTi) alloys with their desirable properties are one of the natural choices of the clinicians. Aim: This study was aimed to compare and rank them based on its tensile strength and electrical resistivity. Materials and Methods: The sample consisted of eight groups of 0.017 inch × 0.025 inch rectangular archwires from eight different manufacturers, and five samples from each group for tensile testing and nine samples for electrical resistivity tests were used. Data for stress at 10% strain and the initial slope were statistically analyzed with an analysis of variance and Scheffe tests with P < 0.05. The stress/strain plots of each product were ranked for superelastic behavior. The rankings of the wires tested were based primarily on the unloading curve's slope which is indicative of the magnitude of the deactivation force and secondarily on the length of the horizontal segment which is indicative of continuous forces during deactivation. For calculating the electric resistivity, the change in resistance after inducing strain in the wires was taken into account for the calculation of degree of martensite transformation and for ranking. Results: In tensile testing Ortho Organizers wires ranked first and GAC Lowland NiTi wires ranked last. For resistivity tests Ormco A wires were found superior and Morelli remained last. Conclusion: these rankings should be correlated clinically and need further studies.

【 授权许可】

Unknown