Pyrolysis Combustion Flow Calorimetry Studies onSome Reactively Modified Polymers

Polymers

Paul Joseph¹  Svetlana Tretsiakova-McNally¹ 

[1] School of the Built Environment and the Built Environment Research Institute, Ulster University, Newtownabbey BT37 0QB, UK;

关键词: chain-growth polymers;    chemical modification;    flame retardance;    pyrolysis combustion flow calorimetry;    heat release rate;    heat release capacity;   

DOI  :  10.3390/polym7030453

来源: DOAJ

【 摘 要 】

As a part of our continuing work to improve the flame retardance of somechain-growth polymers, by employing a reactive route, we have synthesized several unsaturated compounds containing either phosphorus (P), or both phosphorus (P)and nitrogen (N), bearing groups in different chemical environments. They included: diethyl(acryloyloxymethyl)phosphonate (DEAMP); diethyl(1-acryloyloxyethyl)phosphonate (DE1AEP); diethyl-2-(acryloyloxy)ethyl phosphate (DEAEP); diethyl-2-(metharyloyloxy)ethyl phosphate (DEMEP); acrylic acid-2-(diethoxyphosphorylamino)ethyl ester (ADEPAE); acrylic acid-2-[(diethoxyphosphoryl)methyl amino]ethyl ester (ADEPMAE). Acrylonitrile (AN), methyl methacrylate (MMA) and styrene (S) were free radically copolymerisedwith the above mentioned comonomers. The recovered polymers were subjected to routine spectroscopic and thermo-gravimetric analyses. In addition, the combustion behaviours of homopolymers as well as the copolymers containing nominal loadings of P-, or P/N-, groups were, primarily, evaluated using pyrolysis combustion flow calorimetry (PCFC). PCFC has been found to be a very useful screening technique, especially, in establishing the efficacies of the different modifying groups towards flame retarding some base polymeric materials. Values of the heat release capacity (HRC) values normalised to the P contents (wt%) can be considered as useful tool in ranking the various P-containing modifying groups in terms of their efficacies to flame-retard non-halogenated chain-growth polymers considered in the present work.

【 授权许可】

Unknown