Hot Rolling of Magnesium Single Crystals

Metals

JoséAntonio Estrada-Martínez¹  David Hernández-Silva¹  Talal Al-Samman² 

[1] Department of Metallurgical Engineering, Instituto Politécnico Nacional-ESIQIE, 07738 Mexico City, Mexico;Institute for Physical Metallurgy and Materials Physics, RWTH Aachen, 52056 Aachen, Germany;

关键词: magnesium single crystal;    texture;    twinning;   

DOI  :  10.3390/met11030443

来源: DOAJ

【 摘 要 】

To analyze the effect of the initial orientation in the activity of twinning and texture development, magnesium single crystals were rolled at 400 °C (nominal furnace temperature) in two specific orientations. In both orientations, the rolling direction of the sheet (RD) was parallel to the c-axis. For orientation 1, the $\left[11\overline{2}0\right]$ direction was parallel to the normal direction (ND), and for orientation 2, it was parallel to the $\left[10\overline{1}0\right]$ direction. The samples were rolled at 30%, 50% and 80% of thickness reduction. After rolling, all the samples were quenched in water to retain the microstructure. The microstructure and texture evolution were characterized by X-ray diffraction and Electron Backscatter Diffraction (EBSD). The initial single crystals were turned into polycrystals, where most grains had their c-axis almost parallel to the ND, and this reorientation was explained by extension twinning. The active twin variants in orientation 1 aligned the basal plane ~30° from the sheet plane and caused a weaker basal texture compared to orientation 2, where the twin variants aligned the basal plane almost parallel to the sheet plane. Strain localization inside contraction twins was observed, and consequently, non-basal grains nucleated inside these twins and weakened the final basal texture only in orientation 1.

【 授权许可】

Unknown