Microstructure and Properties of CrAlSiN Coatings Deposited by HiPIMS and Direct-Current Magnetron Sputtering

Coatings

Yangmengtian Liang¹  Tiegang Wang¹  Qixiang Fan¹  Zhenghuan Wu¹  Yanmei Liu¹ 

[1] Tianjin Key Laboratory of High Speed Cutting and Precision Machining, Tianjin University of Technology and Education, Tianjin 300222, China;

关键词: CrAlSiN;    microstructure;    Al sputtering power;    mechanical property;   

DOI  :  10.3390/coatings9080512

来源: DOAJ

【 摘 要 】

Four CrAlSiN coatings with different Al contents were prepared by varying Al sputtering power using a combined method of high power impulse magnetron sputtering (HiPIMS) and direct current magnetron sputtering (DCMS). Microstructure, chemical compositions and mechanical properties of the four coatings were characterized by XRD, XPS, SEM, TEM, nano-indentation etc. Results showed that the four coatings possessed face-centered cubic (fcc) CrN phase with Al and part of Si dissolved in it. Another part of Si existed as amorphous phase in the coatings. All the four coatings had columnar structure and formed in epitaxy growth by template effect. With increasing Al sputtering power, the Al content increased from 11.4 to 17.6 at.% gradually, while the Cr content decreased a little. The hardness of the CrAlSiN coatings increased initially probably due to the refinement of the coating grain size, while it decreased afterwards mainly caused by the aggregation of small particles leading to rougher surface and defects formed in the coatings. The elastic modulus and adhesive strength possessed the same variation tendency as the hardness versus Al sputtering power. The CrAlSiN coating with Al sputtering power of about 0.8 kW had the highest hardness of about 26.7 GPa and adhesive strength of about 27.2 N.

【 授权许可】

Unknown