Electrochemical properties of mixed WC and Pt-black powders

Journal of the Serbian Chemical Society

Panić Vladimir V.¹  Obradović Maja D.¹  Babić Biljana M.²  Kowal Andrzej³  Gojković Snežana Lj.⁴ 

[1] Institut za hemiju, tehnologiju i metalurgiju, Beograd;Institut za nuklearne nauke 'Vinča', Beograd;Institute of Catalysis and Surface Chemistry, Polish Academy of Sciences, Krakow, Poland;Tehnološko-metalurški fakultet, Beograd;

关键词: tungsten carbide;    platinum;    hydrogen intercalation;    methanol oxidation;    formic acid oxidation;   

DOI  :  10.2298/JSC0812197O

来源: DOAJ

【 摘 要 】

The electrochemical characteristics of a mixture of Pt-black and WC powders and its catalytic activity for methanol and formic acid oxidation were investigated in acid solution. XRD and AFM measurements revealed that the WC powder employed for the investigation was a single-phase material consisting of crystallites/spherical particles of average size of about 50 nm, which were agglomerated into much larger particles. Cyclic voltammetry showed that the WC underwent electrochemical oxidation, producing tungstate species. In the case of the mixed Pt + WC powders, the tungstate species were deposited on the Pt as a thin film of hydrous tungsten oxide. Enhanced hydrogen intercalation in the hydrous tungsten oxide was observed and it was proposed to be promoted in mixed powders by the presence of hydrogen adatoms on bare Pt sites. The determination of Pt surface area in the Pt + WC layer by stripping of underpotentially deposited Cu revealed that the entire Pt surface was accessible for underpotential deposition of Cu. Investigation of the electrochemical oxidation of methanol and formic acid on Pt + WC and pure Pt layers did not indicate electrocatalytic promotion due to the presence of WC.

【 授权许可】

Unknown