Effect of Ground Tire Rubber (GTR) Particle Size and Content on the Morphological and Mechanical Properties of Recycled High-Density Polyethylene (rHDPE)/GTR Blends

Recycling

Denis Rodrigue¹  Ali Fazli¹ 

[1] Department of Chemical Engineering, Université Laval, Quebec, QC G1V 0A6, Canada;

关键词: recycling;    high-density polyethylene;    ground tire rubber;    thermoplastic elastomer;    particle size;   

DOI  :  10.3390/recycling6030044

来源: DOAJ

【 摘 要 】

This work investigates the effect of ground rubber tire (GRT) particle size and their concentration on the morphological, mechanical, physical, and thermal properties of thermoplastic elastomer (TPE) blends based on recycled high-density polyethylene (rHDPE). In our methodology, samples are prepared via melt blending (twin-screw extrusion followed by compression molding) to prepare different series of blends using GTR with three different particle sizes (0–250 μm, 250–500 μm, and 500–850 μm) for different GTR concentrations (0, 20, 35, 50, and 65 wt.%). The thermal properties are characterized by differential scanning calorimeter (DSC), and the morphology of the blends is studied by scanning electron microscopy (SEM). The mechanical and physical properties of the blends are investigated by quasi-static tensile and flexural tests, combined with impact strength and dynamic mechanical analysis (DMA). The SEM observations indicate some incompatibility and inhomogeneity in the blends, due to low interfacial adhesion between rHDPE and GTR (especially for GTR > 50 wt.%). Increasing the GTR content up to 65 wt.% leads to poor interphase (high interfacial tension) and agglomeration, resulting in the formation of voids around GTR particles and increasing defects/cracks in the matrix. However, introducing fine GTR particles (0–250 μm) with higher specific surface area leads to a more homogenous structure and uniform particle dispersion, due to improved physical/interfacial interactions. The results also show that for a fixed composition, smaller GTR particles (0–250 μm) gives lower melt flow index (MFI), but higher tensile strength/modulus/elongation at break and toughness compared to larger GTR particles (250–500 μm and 500–850 μm).

【 授权许可】

Unknown