Crosslinked PEG and PEBAX Membranes for Concurrent Permeation of Water and Carbon Dioxide

Membranes

George Q. Chen¹  Sandra E. Kentish¹  Hiep T. Lu²  Colin A. Scholes² 

[1] Biomolecular Engineering, The University of Melbourne, Melbourne VIC 3010, Australia;;Peter Cook Centre for Carbon Capture and Storage Research, Department of Chemical &

关键词: carbon dioxide capture;    poly ethylene glycol;    PEBAX;    carbon dioxide;    water;    Lennard Jones;    solubility;   

DOI  :  10.3390/membranes6010001

来源: DOAJ

【 摘 要 】

Membrane technology can be used for both post combustion carbon dioxide capture and acidic gas sweetening and dehydration of natural gas. These processes are especially suited for polymeric membranes with polyether functionality, because of the high affinity of this species for both H2O and CO2. Here, both crosslinked polyethylene glycol diacrylate and a polyether-polyamide block copolymer (PEBAX 2533©) are studied for their ability to separate CO2 from CH4 and N2 under single and mixed gas conditions, for both dry and wet feeds, as well as when 500 ppm H2S is present. The solubility of gases within these polymers is shown to be better correlated with the Lennard Jones well depth than with critical temperature. Under dry mixed gas conditions, CO2 permeability is reduced compared to the single gas measurement because of competitive sorption from CH4 or N2. However, selectivity for CO2 is retained in both polymers. The presence of water in the feed is observed to swell the PEG membrane resulting in a significant increase in CO2 permeability relative to the dry gas scenario. Importantly, the selectivity is again retained under wet feed gas conditions. The presence of H2S is observed to only slightly reduce CO2 permeability through both membranes.

【 授权许可】

Unknown