Behavior of Weld to S960MC High Strength Steel from Joining Process at Micro-Jet Cooling with Critical Parameters under Static and Fatigue Loading

Materials

Tadeusz Szymczak¹  Tomasz Węgrzyn²  Bogusław Łazarz²  Bożena Szczucka-Lasota²  Adam Jurek³ 

[1] Department of Vehicle Type-Approval & Testing, Motor Transport Institute, Jagiellońska 80, 03-301 Warszawa, Poland;Faculty of Transport and Aviation Engineering, Silesian University of Technology, 40-119 Katowice, Poland;Novar Sp. z o. o., Towarowa 2, 44-100 Gliwice, Poland;

关键词: high-strength steel;    components;    joining;    transport;    micro-jet;    welding;   

DOI  :  10.3390/ma14112707

来源: DOAJ

【 摘 要 】

The paper is focused on testing the weld of the S960MC steel produced at the micro-jet cooling under static and fatigue loading at critical parameters. This kind of material was in the form of a sheet with a thickness equal to 2 mm. The joint was obtained using three different types of welding wires: EDFK 1000, Union NiMoCr and Union X96 at the same parameters of the process. The joints were examined using non-destructive and destructive tests. The results from non-destructive experiments enable us to assess the quality of the welds directly before the joining process. In contrast, the destructive one allows following welds behavior under different loading conditions with their critical parameters. The bending experiments confirmed the good plastic properties of the weld, expressed by no cracks in the region tested in many variants of the joint manufactured. The results from static tests indicated a significant reduction of mechanical parameters of the weld in comparison to the base metal, expressed by 50% differences. Fatigue data have enabled us to follow the welding behavior at the increasing amplitude of axial stress up to fracture at constant amplitude value covering the following values of stress 650 MPa–100 MPa. Variations of total energy are presented at different values of several cycles up to fracture. Fracture regions are collected for analysis of the joint region features under cyclic loading. They have indicated differences in weld cracking depended on the stress level. Finally, the Wöhler S-N curve of the weld was determined, indicating the value of the fatigue limit of the weld tested, i.e., 100 MPa. The weld at the Union NiMoCr welding wire was indicated as the joint having the highest resistance on static and fatigue loadings.

【 授权许可】

Unknown