Synthesis and Characterization of BaTiO3/Polypyrrole Composites with Exceptional Dielectric Behaviour

Polymers

Shahid Atiq¹  Shahid M. Ramay²  Nasser S. Alzayed²  Syed Mansoor Ali²  Khalil Ahmed³  Rabia Rehman³  Farah Kanwal³ 

[1] Centre of Excellence in Solid State Physics, University of the Punjab, Lahore 54590, Pakistan;Department of Physics and Astronomy, College of Science, King Saud University, P.O. Box 2455, Riyadh 11451, Saudi Arabia;Institute of Chemistry, University of the Punjab, Lahore 54590, Pakistan;

关键词: barium titanate;    polypyrrole;    dielectric behaviour;    polymerization;   

DOI  :  10.3390/polym10111273

来源: DOAJ

【 摘 要 】

Higher concentrations of ceramic fillers induce brittleness in the ceramic/polymer hybrids which restrict their applications to limited fields especially when such hybrids are prepared for their use as dielectrics. We have synthesized and characterized different BaTiO₃-polypyrrole (PPy) composites by changing the concentration of BaTiO₃ from 1% by weight of PPy taken to 5 wt % to explore its effect on the dielectric parameters of the final product and found that the BaTiO₃-polypyrrole composite with weight ratio of 0.05:1 exhibited highest dielectric constant, lowest dielectric loss and thermally most stable. All the composites were prepared using in-situ polymerization of pyrrole in an aqueous dispersion of low content of BaTiO₃ in the presence of small amount of Hydrochloric acid. These composites were characterized for their microstructure and crystallinity by X-ray diffractometer (XRD), Fourier transform infrared (FT-IR) spectroscopy and scanning electron microscopy (SEM) while thermal stability by thermo gravimetric (TGA) analysis. An impedance analyser (LCR meter) was utilized to investigate the dielectric parameters. FT-IR data confirmed the presence of the two phases and their interaction, inferred from the shifting of normal PPy peaks. The data obtained from XRD confirmed the presence of crystallites of 2.8 to 5 nm with dominant crystallinity of the filler, TGA analysis (25 to 600 °C) confirmed the higher thermal stability induced on successive addition of the filler into the prepared composites as compared to that of pure PPy in a wide temperature range which is unusual for such a low % age addition of the filler. The SEM analysis together with XRD results reveal that the successive introduction of BaTiO₃ particles produced crystallites of 2 to 5 nm size which bonded together and changed the hemispherical shaped larger grains of the matrix to regular shaped smaller grains. The dielectric constant of the composites was enhanced with filler contents from 178 to 522 at 1 MHz for 1 wt % and 5 wt % BaTiO₃ respectively. It was concluded that the introduction of BaTiO₃ into the polymer matrix with this new procedure has greatly affected the polymerization process, thermal stability, morphology and dielectric properties of the host matrix and has resulted in a novel series of the composites which may have broad applications.

【 授权许可】

Unknown