Influence of powder particle size on the microstructure of a hot isostatically pressed superalloy

Journal of Materials Research and Technology

Pingxiang Zhang¹  Shujin Liang²  Jiaming Song²  Qingxiang Wang²  Zonghong Qu³  Yunjin Lai³ 

[1] Sino-Euro Materials Technologies of Xi'an Co., Ltd, Xi'an, 710018, China;Sino-Euro Materials Technologies of Xi'an Co., Ltd, Xi'an, 710018, China;State Key Laboratory of Solidification Processing, Northwestern Polytechnical University, Xi'an, 710072, China;

关键词: Powder particle size;    Hot isostatic pressing;    Plasma rotating electrode process;    Previous particle boundaries;    FGH97;   

DOI  :  

来源: DOAJ

【 摘 要 】

The influence of powder particle size on the microstructure of the powder metallurgy superalloy FGH97 was investigated. The powder atomized by the plasma rotating electrode process was sieved to three types: fine powder (0–53 μm), medium-sized powder (53–150 μm), and coarse powder (150–212 μm), which were all characterized by their nearly perfect spherical shape and low oxygen content. The powder was filled, degassed, sealed, and then densified by hot isostatic pressing. Then the microstructures of the fully dense compacts were characterized. The results show that fine powder led to limited plastic deformation of particles during densification, resulting in a minimum of Σ3 boundaries and modest PPB (Previous Particle Boundary) decoration. The fine powder compact showed that low impact toughness was caused by fracture along the PPB. However, the addition of Nb and Hf promoted the formation of the dispersed stable MC particles inside the grain, thus preventing the diffusion of C to the surface of the powder particles to form M6C carbides, and resulting in little tendency to present PPB for this alloy. Therefore, the medium-sized powder and coarse powder compact did not present PPB. Thus, the medium-sized powder is optimal for HIP compact preparation, given that fine powder produced PPB while the coarse powder increased the grain size.