Effect of anionic group [SiO4]4−/[PO4]3− on the luminescence properties of Dy3+-doped tungstate structural compounds

Journal of Advanced Ceramics

Lefu Mei¹  Jianxiong Bin¹  Ze Zhang¹  Ning Liu²  Zhijian Peng² 

[1] Beijing Key Laboratory of Materials Utilization of Nonmetallic Minerals and Solid Wastes, National Laboratory of Mineral Materials, School of Materials Sciences and Technology, China University of Geosciences (Beijing);School of Science, China University of Geosciences (Beijing);

关键词: phosphors;    scheelite structure;    luminescence property;    anion substitution;   

DOI  :  10.1007/s40145-021-0478-x

来源: DOAJ

【 摘 要 】

Abstract Novel scheelite structures of Li2Ca(WO4)2, Li2Ca2(WO4)(SiO4), and LiCa2(WO4)(PO4) fluorescent materials were successfully prepared using a high-temperature solid-phase process. The compounds were characterized by X-ray diffraction and energy dispersive spectroscopy. The tests revealed that the substitution of [WO4]2− by [SiO4]4− or [PO4]3− tetrahedron in tungstate had no significant influence on the crystal structure of the Li2Ca(WO4)2. When Dy3+ ions were introduced as an activator at an optimum doping concentration of 0.08 mol%, all of the as-prepared phosphors generated yellow light emissions, and the emission peak was located close to 576 nm. Replacing [WO4]2− with [SiO4]4− or [PO4]3− tetrahedron significantly increased the luminescence of the Li2Ca(WO4)2 phosphors. Among them, the LiCa2(WO4)(PO4):0.08Dy3+ phosphor had the best luminescence properties, decay life (τ = 0.049 ms), and thermal stability (87.8%). In addition, the as-prepared yellow Li2Ca(WO4)2:0.08Dy3+, Li2Ca2(WO4)(SiO4):0.08Dy3+, and LiCa2(WO4)(PO4):0.08Dy3+ phosphor can be used to fabricate white light emitting diode (LED) devices.

【 授权许可】

Unknown