Grain size effect on piezoelectric properties of Sr2Nb2O7 ceramics

Journal of Advanced Dielectrics

Ruihong Liang¹  Tao Chen¹  Zhiyong Zhou¹  Xianlin Dong¹ 

[1] Shanghai Institute of Ceramics, Key Laboratory of Inorganic Functional Materials and Devices, Chinese Academy of Sciences, 1295 Dingxi Road, Shanghai 200050, P. R. China;

关键词: Grain size;    piezoelectric properties;    layer structure;   

DOI  :  10.1142/S2010135X18200035

来源: DOAJ

【 摘 要 】

Grain size effect on piezoelectric properties and thermal stability of perovskite layer structured (PLS) Sr2Nb2O7 ceramics are investigated. The Sr2Nb2O7 ceramics with different average grain sizes from 1.2μm to 3.6μm were prepared in different sintering temperatures by solid state reaction method. The average grain size increases, accompanied by a higher relative density of up to 96%. Pure Sr2Nb2O7 ceramics with larger grain size show a remarkable d33 of (1.7±0.1)pC/N while still with a very high Tc of (1340±4)∘C. The thermal depolarization temperature of samples with large grain sizes reach over 1200∘C and the thermal stability increased with increasing of grain size. The ferroelectric domains structure was observed by PFM and larger grain is easy to form ferroelectric domain then enhance piezoelectric properties. This study demonstrates enhanced piezoelectric properties can be achieved in pure Sr2Nb2O7 by solid state reaction method and bring great revitalization to the Sr2Nb2O7-based ceramics as a promising high-temperature piezoelectric material.

【 授权许可】

Unknown