Impact Performance and Bending Behavior of Carbon-Fiber Foam-Core Sandwich Composite Structures in Cold Arctic Temperature

Journal of Composites Science

M.H. Khan¹  K.T. Tan¹  Bing Li² 

[1] Department of Mechanical Engineering, The University of Akron, Akron, OH 44325-3903, USA;School of Aeronautics, Northwestern Polytechnical University, Xi’an 710072, China;

关键词: composite sandwich structure;    impact performance;    bending behavior;    arctic temperature;   

DOI  :  10.3390/jcs4030133

来源: DOAJ

【 摘 要 】

This study investigates the impact performance, post-impact bending behavior and damage mechanisms of Divinycell H-100 foam core with woven carbon fiber reinforced polymer (CFRP) face sheets sandwich panel in cold temperature Arctic conditions. Low-velocity impact tests were performed at 23, −30 and −70 °C. Results indicate that exposure to low temperature reduces impact damage tolerance significantly. X-ray microcomputed tomography is utilized to reveal damage modes such as matrix cracking, delamination and fiber breakage on the CFRP face sheet, as well as core crushing, core shearing and debonding in the Polyvinyl Chloride (PVC) foam core. Post-impact bending tests reveal that residual flexural properties are more sensitive to the in-plane compressive property of the CFRP face sheet than the tensile property. Specifically, the degradation of flexural strength strongly depends on pre-existing impact damage and temperature conditions. Statistical analyses based on this study are employed to show that flexural performance is dominantly governed by face sheet thickness and pre-bending impact energy.

【 授权许可】

Unknown