Accurate Estimation of Yield Strength and Ultimate Tensile Strength through Instrumented Indentation Testing and Chemical Composition Testing

Materials

Martin Scales¹  Jeffrey A. Kornuta¹  Ramon Gonzalez²  Peter Veloo²  Nathan Switzner³  Joel Anderson³ 

[1] Exponent, Inc., Houston, TX 77042, USA;Pacific Gas & Electric Company, Walnut Creek, CA 94598, USA;RSI Pipeline Solutions, New Albany, OH 43054, USA;

关键词: IIT;    nondestructive testing;    integrity;    pipelines;    materials verification;   

DOI  :  10.3390/ma15030832

来源: DOAJ

【 摘 要 】

Federal rule changes governing natural gas pipelines have made non-destructive techniques, such as instrumented indentation testing (IIT), an attractive alternative to destructive tests for verifying properties of steel pipeline segments that lack traceable records. Ongoing work from Pacific Gas and Electric Company’s (PG&E) materials verification program indicates that IIT measurements may be enhanced by incorporating chemical composition data. This paper presents data from PG&E’s large-scale IIT program that demonstrates the predictive capabilities of IIT and chemical composition data, with particular emphasis given to differences between ultimate tensile strength (UTS) and yield strength (YS). For this study, over 80 segments of line pipe were evaluated through tensile testing, IIT, and compositional testing by optical emission spectroscopy (OES) and laboratory combustion. IIT measurements of UTS were, generally, in better agreement with destructive tensile data than YS and exhibited about half as much variability as YS measurements on the same sample. The root-mean squared error for IIT measurements of UTS and YS, respectively, were 27 MPa (3.9 ksi) and 43 MPa (6.2 ksi). Next, a machine learning model was trained to estimate YS and UTS by combining IIT with chemical composition data. The agreement between the model’s estimated UTS and tensile UTS values was only slightly better than the IIT-only measurements, with an RMSE of 21 MPa (3.1 ksi). However, the YS estimates showed much greater improvement with an improved RMSE of 27 MPa (3.9 ksi). The experimental, mechanical, and metallurgical factors that contributed to IIT’s ability to consistently determine destructive UTS, and the differences in its interaction with composition as compared to YS, are discussed herein.