The Strength of the Adhesive Joints of the Medium-Density Fireboards and Particle Boards with the PVC Film

Advances in Sciences and Technology

Mirosław Müller¹  Vlodymyr Iasnii²  Tatiana Vitenko²  Anna Rudawska³  Dana Stančeková⁴ 

[1] Czech University of Life Science Prague, Faculty of Engineering, 165 21, Prague, Czech Republic;Ivan Puluj TNTU, Faculty of Engineering of Machines, Structures and Technologies, Ruska 56 Street, 46001 Teronpil, Ukraine;Lublin University of Technology, Faculty of Mechanical Engineering, ul. Nadbystrzycka 36, 20-618 Lublin, Poland;University of Žilina, Faculty of Mechanical Engineering, Univerzitna 1, 010 26, Žilina, Slovakia;

关键词: adhesive joints;    strength;    mdf;    particle board;    pvc film;   

DOI  :  10.12913/22998624/113612

来源: DOAJ

【 摘 要 】

The aim of the present article was to analyse the adhesive joints of different types of the furniture boards used for the furniture production. The present article included a comparative analysis of the adhesive joints of the particle board and the medium-density fireboard (MDF) pressed with the following types of film: A 0.3 mm thick PVC film and a 0.8 mm thick acrylic film, made with use of a single-component reac-tive hot-melt adhesive based on the PUR 706.2 ME polyurethane. It was observed that, among others, the adhesive joints made of the particle board with a pressed 0.3 mm thick PVC film and the adhesive’s basis weight of 24 g/m2 is characterised by better strength properties than the adhesive joints of the particle board with the adhesive’s basis weight of 48 g/m2.

【 授权许可】

Unknown