Mechanical Behavior Modelling and Filler Geometry Effect of Glass Filler Reinforced Starch-Epoxy Hybrid Matrix Composites

Materials

Foteini K. Kozaniti¹  Lykourgos C. Kontaxis¹  George C. Papanicolaou¹ 

[1] Composite Materials Group, Department of Mechanical Engineering and Aeronautics, University of Patras, GR 265 04 Patras, Greece;

关键词: starch;    epoxy;    glass fillers;    hybrid polymer matrix;    flexural modulus;    flexural strength;   

DOI  :  10.3390/ma14216587

来源: DOAJ

【 摘 要 】

The aim of the present study is to investigate the inclusion geometry and concentration effect on the quasi-static properties of a starch-epoxy hybrid matrix composite. The composites investigated consisted of a starch-epoxy hybrid matrix reinforced with four different glass inclusions such as 3 mm long chopped strands, 0.2 mm long short glass fibers, glass beads (120 μm in diameter) and glass bubbles (65 μm in diameter) at different concentrations. The flexural modulus and the strength of all materials tested were determined using three-point bending tests. The Property Prediction Model (PPM) was applied to predict the experimental findings. The model predicted remarkably well the mechanical behavior of all the materials manufactured and tested. The maximum value of the flexural modulus in the case of the 3 mm long chopped strands was found to be 75% greater than the modulus of the hybrid matrix. Furthermore, adding glass beads in the hybrid matrix led to a simultaneous increase in both the flexural modulus and the strength.

【 授权许可】

Unknown