Electrochemical Corrosion and Metal Ion Release Protective Efficiency of the Multilayer TaN Coatings on CoCrMo Biomedical Alloy

Medžiagotyra

Ali Kemal ASLAN¹  Mehmet Sami GÜLER²  Erkan BAHÇE³ 

[1] Department of Machinery and Metal Technologies, Munzur University, Tunceli, Turkey,;Department of Machinery and Metal Technologies, Ordu University, Ordu, Turkey;Department of Mechanical Engineering, İnonu University, Malatya, Turkey;

关键词: cocrmo;    biomaterial;    multilayer coating;    corrosion;    metal ion release;   

DOI  :  10.5755/j02.ms.27695

来源: DOAJ

【 摘 要 】

CoCrMo alloy is widely used in artificial orthopedic joint applications due to its high mechanical properties. But, high levels of the metal ion release from alloy surfaces cause variable toxic and allergic effects on the patient in vivo use. This case restricts the lifetime of the implant and results in the failure of the artificial joint. In order to enhance the corrosion resistance and to decrease the metal ion release, alloy surface was multilayer-coated by closed field unbalanced magnetron system. The protective efficiency of the coatings was determined by potentiodynamic polarization tests and static immersion tests were performed for 45, 60 and 90 days in the simulated body fluid in order to understand the effect of the coatings on the metal ion release. The metal ion concentrations in the simulated body fluids were determined by using inductively coupled plasma mass spectrometry device. The electrochemical corrosion results showed that the multilayer coatings provided 93 % protective efficiency in terms of corrosion resistance. Multilayer coatings decreased the metal ions release levels significantly, especially Co leaking was decreased approximately 52 times compared to uncoated samples.

【 授权许可】

Unknown