Annealing Effects in Twin-Roll Cast AA8006 Aluminium Sheets Processed by Accumulative Roll-Bonding

Materials

Michaela Poková¹  Miroslav Cieslar¹ 

[1] Faculty of Mathematics and Physics, Charles University in Prague, Ke Karlovu 5, CZ-121 16 Prague 2, Czech Republic;

关键词: accumulative roll-bonding;    AA8006;    recrystallization;    twin-roll cast;   

DOI  :  10.3390/ma7128058

来源: DOAJ

【 摘 要 】

Ultrafine grained sheets were prepared from a twin-roll cast AA8006 aluminium alloy using accumulative roll-bonding process at room temperature. The evolution of microstructure of sheets after three accumulative roll-bonding passes during isochronal annealing with a constant step of 20 °C/20 min was studied by light and electron microscopy. The influence of the resulting microstructure on mechanical properties was monitored by microhardness measurements. The microhardness increases when the material is annealed up to 160 °C. Above this temperature a fast drop of microhardness occurs followed by a negligible variation at annealing temperatures exceeding 300 °C. In order to map continuously the microstructure changes during annealing, the in situ TEM experiments in the heating stage were performed as a supplement to post-mortem TEM observations.

【 授权许可】

Unknown