Study of the Properties of Full Component Recycled Dry-Mixed Masonry Mortar and Concrete Prepared from Construction Solid Waste

Sustainability

Qiuyi Li¹  Zhenwen Hu¹  Junzhe Liu¹  Yuanxin Guo¹  Zhe Kong²  Dunlei Su³  Guisheng Cai⁴  Shidong Zheng⁵ 

[1] College of Architectural Engineering, Qingdao Agricultural University, Qingdao 266109, China;Qingdao Real Estate Vocational Secondary Specialized School, Qingdao 266034, China;School of Traffic Civil Engineering, Shandong Jiaotong University, Jinan 250357, China;Shandong Academy of Building Research Co., Ltd., Jinan 255000, China;Shandong Junhong Environmental Technology Co., Ltd., Zibo 255000, China;

关键词: recycled aggregate;    recycled powder (RP);    recycled concrete;    performance test;    microstructure;    interface transition zone;   

DOI  :  10.3390/su13158385

来源: DOAJ

【 摘 要 】

Solutions are needed to solve the problem of a large amount of construction solid waste and a shortage of natural aggregate (coarse and fine aggregates). In this paper, simple-crushed coarse aggregate (SCRCA) and simple-crushed fine aggregate (SCRFA) were obtained by simple-crushing of construction solid waste. On this basis, SCRCA and SCRFA were treated with particle-shaping to obtain particle-shaping coarse aggregate (PSRCA) and particle-shaping fine aggregate (PSRFA), and the recycled powder (RP) produced in the process of particle-shaping was collected. Under the condition of a 1:4 cement-sand ratio, RP was used to replace cement with four substitution rates of 0, 10%, 20%, and 30%, and dry-mixed masonry mortar was prepared with 100% SCRFA, PSRFA, and river sand (RS). The basic and mechanical properties and microstructure of hydration products of dry-mixed mortar were analyzed, and the maximum substitution rate of RP was determined. Under the condition that the amount of cementitious material is 400 kg/m³ and the RP is at the maximum replacement rate, three different aggregate combinations to prepare concrete are the 100% use of SCRCA and SCRFA, PSRCA and PSRFA, and RS and natural aggregate (NCA); the workability, mechanical properties, and aggregate interface transition zone of the prepared concrete were analyzed. The results show that when the replacement rate of RP is less than 20%, it has little effect on the properties of products. The performance of PSRCA and PSRFA after treatment is better than that of SCRCA and SCRFA. Under different RP substitution rates, the performance of dry-mixed mortar prepared with PSRFA is very close to that prepared with RS. The performance of recycled concrete prepared with PSRCA and PSRFA is also very close to that of products prepared with NCA and RS. The failure morphology of PSRCA and RSRFA concrete is also similar to that of NCA and RS concrete.