Effect of Interfacial Structure on Mechanical Properties of Graphene Reinforced Al2O3–WC Matrix Ceramic Composite

Nanomaterials

Xuchao Wang¹  Xianhua Tian¹  Enzhao Cui¹  Jun Zhao¹  Zhefei Sun¹ 

[1] Key Laboratory of High Efficiency and Clean Mechanical Manufacture of MOE, School of Mechanical Engineering, Shandong University, Jinan 250061, China;

关键词: ceramic composite;    graphene;    interface;    first-principles;    mechanical properties;   

DOI  :  10.3390/nano11061374

来源: DOAJ

【 摘 要 】

The interfacial structures and interfacial bonding characteristics between graphene and matrix in graphene-reinforced Al₂O₃–WC matrix ceramic composite prepared by two-step hot pressing sintering were systematically investigated. Three interfacial structures including graphene–Al₂O₃, graphene–Al₂OC and graphene-WC were determined in the Al₂O₃–WC–TiC–graphene composite by TEM. The interfacial adhesion energy and interfacial shear strength were calculated by first principles, and it has been found that the interfacial adhesion energy and interfacial shear strength of the graphene–Al₂OC interface (0.287 eV/nm², 59.32 MPa) were far lower than those of graphene–Al₂O₃ (0.967 eV/nm², 395.77 MPa) and graphene–WC (0.781 eV/nm², 229.84 MPa) interfaces. Thus, the composite with the strong and weak hybrid interfaces was successfully obtained, which was further confirmed by the microstructural analysis. This interfacial structure could induce strengthening mechanisms such as load transfer, grain refinement, etc., and toughening mechanisms such as crack bridging, graphene pull-out, etc., which effectively improved mechanical properties.

【 授权许可】

Unknown