Effect of heating/cooling rate on the properties of BaTiO3 ceramics

Songklanakarin Journal of Science and Technology (SJST)

关键词: BaTiO3 ceramics;    heating/cooling rate;    dielectric constant;   

DOI  :  

来源: DOAJ

【 摘 要 】

The effect of heating/cooling rate on the physical, microstructural and dielectric properties of BaTiO3 ceramics has been studied. The heating/cooling rate using in this work is ranged from 10 to 20ºC/min at sintering temperature of 1350ºC for 2 hours. It was found that the physical properties of the barium titanate ceramics using heating/cooling rate of 20ºC/min gave a higher value of percent shrinkage and density than that of 10 and 15ºC/min. From the dielectric constant measurement, the maximum dielectric constant depended very much on the heating/cooling rates. The maximum dielectric constant of the ceramics using heating/ cooling rate of 20ºC/min was higher that that of 10 and 15ºC/min. Hence, the small grain size and high density of the ceramics using high heating/cooling rate may have an influence on the value of maximum dielectric properties of the BaTiO3 ceramics.

【 授权许可】

Unknown