Influence of Multi-Pass Hot Extrusion on Microstructure and Mechanical Properties of the Mg–4Zn–1.2Y–0.8Nd Alloy

Crystals

Beining Du¹  Hui Zhao²  Liyuan Sheng³  Xingru Zhang³  Yufeng Zheng³  Tingfei Xi³ 

[1] PKU-HKUST Shenzhen-Hong Kong Institution, Shenzhen 518057, China;School of Materials Science and Engineering, Xi’an Shiyou University, Xi’an 710065, China;Shenzhen Institute, Peking University, Shenzhen 518057, China;

关键词: hot extrusion;    Mg–Zn–Y–Nd alloy;    microstructure;    mechanical properties;   

DOI  :  10.3390/cryst11040425

来源: DOAJ

【 摘 要 】

In the present research, a Mg–4Zn–1.2Y–0.8Nd (wt.%) alloy was heat treated and hot extruded with different passes. XRD, SEM, TEM and tensile testing were employed to characterize the microstructure evolution and mechanical properties. The results exhibited that the semi-continuously distributed W-Mg₃Zn₃Y₂ phases formed the skeleton structure which separated the α-Mg matrix into a dual-size grain structure. In addition, the Mg₂₄Y₅, Mg₄₁Nd₅ and Y₂O₃ phase was also observed in the heat-treated alloy. Moreover, it was found that the Mg24Y5 phase had an orientation relationship with the α-Mg matrix of α${[111]}_{\mathrm{Mg}24\mathrm{Y}5}//{[0001]}_{\mathsf{\alpha }-\mathrm{Mg}}$ and α${(10\overline{1})}_{\mathrm{Mg}24\mathrm{Y}5}//{(10\overline{1}0)}_{\mathsf{\alpha }-\mathrm{Mg}}$, and the Mg₄₁Nd₅ phase had an orientation relationship with the α-Mg matrix of α${[001]}_{\mathrm{Mg}41\mathrm{Nd}5}//{[0001]}_{\mathsf{\alpha }-\mathrm{Mg}}$. The one-pass hot extrusion segmented the secondary phases into small ones and refined the α-Mg matrix. Due to the partly recrystallization and crystal orientation difference, the coarse elongated grain surrounded by fine recrystallized grain and secondary phase was the main feature of the one-pass hot extruded alloy. Furthermore, the secondary phases exhibited the linear distribution along the direction of hot extrusion. The two-pass hot extrusion refined the secondary phase and matrix further, which produced the ultrafine α-Mg matrix with uniform grain size and a well redistributed secondary phase. Due to the microstructure optimization by the multi-pass hot extrusion, the ductility and strength of the Mg–Zn–Y–Nd alloy were well improved, especially the two-pass hot extruded alloy which was significant improved in ductility and strength simultaneously.

【 授权许可】

Unknown