Correlation between the Liquid Fraction, Microstructure and Tensile Behaviors of 7075 Aluminum Alloy Processed by Recrystallization and Partial Remelting (RAP)

Metals

Dong Yang¹  Jinlong Fu¹  Kaikun Wang¹ 

[1] School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China;

关键词: aluminum;    liquid droplets;    tensile properties;    semisolid;    fracture mechanisms;   

DOI  :  10.3390/met8070508

来源: DOAJ

【 摘 要 】

The recrystallization and partial remelting (RAP) method was applied to obtain the semisolid 7075 aluminum alloy with different liquid fractions. The effects of liquid fraction on the microstructure and tensile properties were determined in detail. The results show that during the semisolid isothermal treatment, the number of the intra-granular liquid droplets increased initially with the melting of the eutectic phases. Extension of isothermal soaking led to the coarsening and spheroidization of the intra-granular droplets. Finally, these liquid droplets merged and moved towards the grain exterior. The room temperature tensile strength of the RAP-processed AA7075 alloy, which were isothermally soaked at 600 and 610 °C, increased with the holding time from 5 to 15 min and then decreased dramatically from 15 to 25 min, whilst that soaked at 620 °C decreased monotonously. The fracture morphology exhibited intra-granular fracture mode at low liquid fractions. However, it transformed to a completely brittle and inter-granular type at high liquid fractions and the cohesive force of the liquid-solid interfaces at the grain boundaries determined the strength of the alloys. The transfer of the intra-granular liquid droplets into the inter-granular liquid phase played a significant role for the different fracture behaviors of the RAP-processed AA7075 alloy. The paper provides some reference for better controlling the microstructure and mechanical properties in semisolid processing.

【 授权许可】

Unknown