Effect of Surface Mechanical Attrition Treatment on Torsional Fatigue Properties of a 7075 Aluminum Alloy

Metals

Delphine Retraint¹  Zhidan Sun¹  Pengfei Gao¹  Hongqian Xue²  Tao Gao²  Yizhuo Li³ 

[1] LASMIS, University of Technology of Troyes (UTT), 10004 Troyes, France;School of Mechanical Engineering, Northwestern Polytechnical University, Xi’an 710072, China;Xi’an Modern Chemistry Research Institute, Xi’an 710065, China;

关键词: torsional fatigue;    aluminum alloy;    SMAT;    fatigue life;    fracture mechanism;   

DOI  :  10.3390/met12050785

来源: DOAJ

【 摘 要 】

The effect of Surface Mechanical Attrition Treatment (SMAT) on torsional fatigue properties of a 7075 aluminum alloy was investigated. A number of fatigue samples were heat treated to increase the sensitivity of the material to SMAT. Compared with the as-machined (AM) samples, the fatigue lives of their SMATed counterparts (AM-SMAT) tested under torsional loading increased under high stress amplitudes, but decreased under low amplitudes. However, the fatigue lives of heated and SMATed samples (HT-SMAT) increased under all the investigated stress amplitudes, compared with those that were heat treated (HT). It was also revealed that the cracking mechanisms are different for the samples in different states, and they are dependent on the imposed stress levels. The results show that SMAT could have both beneficial and detrimental effects on the fatigue lives depending on the testing conditions. The roles played by various factors, including residual stresses, grain refinement, and surface roughness, were analyzed and discussed to interpret the results.

【 授权许可】

Unknown