Size controllable synthesis of ZSM-5 zeolite and its catalytic performance in the reaction of methanol conversion to aromatics

Royal Society Open Science

Hongxue Qi¹  Yi-en Du¹  Xianjun Niu¹  Yang Bai¹  Yongqiang Chen¹ 

[1] Department of Chemistry and Chemical Engineering, Jinzhong University, Jinzhong, Shanxi 030619, People's Republic of China;

关键词: silicalite-1;    ZSM-5 zeolites;    crystal size;    methanol to aromatics;   

DOI  :  10.1098/rsos.211284

来源: DOAJ

【 摘 要 】

ZSM-5 zeolites were hydrothermally synthesized with commercial silica sol, and the crystal size was controlled by adding silicalite-1 seed in the synthetic system. The crystal size of ZSM-5 was affected by the crystallization time of seed, seed content and seed size. ZSM-5 zeolites with controllable particle size in the range of 200–2200 nm could be obtained. The prepared samples with different particle sizes were used for the reaction of methanol conversion to aromatics (MTA). The results suggested that the HZSM-5 catalyst with small crystal size showed much longer catalyst lifetime and higher selectivity for C5+ hydrocarbons and aromatics, especially C9+ aromatics in the MTA reaction. Moreover, the introduction of zinc (Zn) into the HZSM-5 zeolites can considerably promote the selectivity to aromatics in the products. Zn modified HZSM-5 zeolites with different Zn loading amounts were prepared by the incipient wetness impregnation method, and the highest aromatics selectivity was obtained when the Zn loading was 1.0%. The improvement of methanol aromatization was ascribed to the synergistic effect of Brønsted acid sites and the newly formed Zn-Lewis acid sites.

【 授权许可】

Unknown